ProfiRS anticorrosive epoksüüdkrunt 4: 1 grey set hardener 1L

TOOTED
anticorrosive epoksüüdkrunt 4: 1 grey
hardener 1: 4 epoksüpraimeri ..

TOOTEKIRJELDUS
high-quality 2-component epoksükrunt anti corrosion additives. Excellent,
protects teraspindu against corrosion car repair käigus.  can implement "wet wet" tehnikaga.
✓ Teraspindade perfect protection.
✓ very good adhesiveness different aluspindadega.
✓ easy segamis- and pealekandmisprotsess.
✓ especially smooth fluidity.

Läikeaste - Matt.

base surface making
anti-corrosion epoksüüdkruntvärvi may apply following aluspindadele:
✓ steel and aluminium after mattimist and rasvatustamist.
✓ zinc plated steel, galvanized after karestamist and rasvatustamist.
✓ grinded polüesterklaas (GFK / GRP) and epoksiidklaaslaminaadid.
✓ Polyester- and epoksiidpahtlid.
✓ old covers in good condition after mattimist and rasvatustamist.

best remonditulemuse to achieve on important surface good preparation.
It is recommended lihvpaberit next gradatsiooniga:
by hand grinding (dry or wet): P280 - P320 (GRP P400).
Masinlihvimine (dry): P180 ÷ P220.

application
for cars for repair
Segamise ratio (capacity / pc)
primer 4
hardener  1
solvent 15-50%

mix carefully, up to saadakse homogeenne Consistency.
Pihustus viscosity
55 - 60 seconds 20oC at 15% lahjenduses
35 - 40 seconds 20oC at 25% lahjenduses
18 - 20 seconds 20oC at 50% lahjendusega

mixture Serviceable life
approximately 3 hours 20 ° C at
layers number: 2 - 3 layers.
recommended cover thickness pc  kruntvärvi .: 50 ÷ 70 µm dry kihid.
recommended film thickness lihvtäite .
200–250 µm dry layer
Paint Sprayer gun parameetrid:
nozzle: 1,6 - 2,0 mm; Sisendrõhk: 2,0–2,2 baari.
HVLP gun parameetrid
nozzle: 1,5 - 1,9 mm; Sisendrõhk: 2,0 baari.
evaporation time
layers vahel: 5 - 10 minutes
before kuumendamist: approximately 10 minutes
before pealiskihti (wet wet): 60 - 120 minutes
evaporation time depends temperature and layer thickness.

drying time
approximately 8 hours at temperature 20 ° C (depending on layer thickness).
approximately  45 minutes at temperature  60 ° C (depending on layer thickness).
temperature alla 20 ° C prolongs significantly kõvenemisaega.

IR kuivatamine
17 - 22 minutes lühilaineid thickness 150 - 200 µm.
dry grinding
machine grinding: P360 - P500.
by hand grinding: P280 - P320.
wet grinding
machine grinding: P600 - P1000
by hand grinding: P800 - P1000.

Kahekomponendilistele epoksükruntidele can apply following:
✓ 2-komponendilised pealiskihid.
✓ 1-komponendilised alusvärvid.
✓ 2-komponendilised akrüülkruntvärvid.
✓ 2-komponendilised polüesterpahtlid.
✓ 2-komponendilised epoksütäiteained.

ÜLDMÕTTED
✓ don't exceed recommended hardener quantity!
✓ best results will be achieved at room temperature colours. Ümbritsev temperature
and rakendatava Product temperature peaks be similar.
✓ Kahekomponendiliste toodetega working is recommended to use kaitsevahendeid. to protect to eyes and hingamisteid.
Ruumid peaksid be well ventileeritud.
✓ tools black pesta immediately after applying.
✓ Ülaltoodud product no saa to use reaktiivsete kruntidega  and 1K kruntidega.